industrial repair agent > high temperature iron repair agent compound epoxy coating

high temperature iron repair agent compound epoxy coating

BD116 metal iron high temperature resistant repair agent rebulding compound epoxy coating

Product description of our BD116 high temperature resistant iron metal repair agent epoxy coating compound:
It’s the high temperature high performance polymerization metal materials compounded by various alloy material
and modified toughening heat resistant resin.The highest temperature resistance is 300 degree,suitable for the
repairing of gray iron,ductile iron,cast iron parts defect and iron parts wear under the high temperature
working condition.The color after repairing is basically the same as the substrates,with the very high strength and
excellent wear&corrosion resistance and aging resistant properties,can do various mechanical processing
together with substrates.

Performance index:

product name	physical state	standard packaging	volume (cm3)	operational time limit (25℃)	usable time (25℃)
BD116 high temperature metal iron repair agent rebuilding epoxy compound	paste	250g/set Two-component	178	45min	24h

color	density (g/cm3)	compressive strength (Mpa) GB1041-2008	shear strength (Mpa) GB7124-2008	bending strength (Mpa) GB1042-1999	hardness （Shore D） ASTM-D-2556	working temperature （℃）
iron cast	1.41	97	15	48	86	-60～250

How to use:
1.Surface treatment: Do the coarsening treatment on the pending-repair or needing-bonding area,
then clean it by cleaning agent.

2.Configuration: According to the mass ratio A:B=4:1 or volume ratio A:B=4:1,make A and B two components mix uniformly,
then use it up within specified operation time limit.

3.Coating: Make the mixed-up material spread coating on the pending-repair areas layer by layer,the first layer should be compacted,make it infiltrate fully with the substrates.
If the following working procedure needs machining,should keep out appropriate machining allowance

4.Curing: cure for 2 hours at the temperature of 25～30 degree,heat it up to the temperature of 80 degree and keep this temperature for 2 hours or cure for 24 hours at the temperature of 25～30 degree before using,if the temperature is low,should heat it up or prolong the curing time to promote the curing.

Packaging specification:
Two-component,250g/set,8 sets/carton or 16 sets/carton.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 24 months.Avoid placing it upside down,
knocking against and transporting it as a non-dangerous product during transportation.

Product packaging photo of BD116 metal iron high temperature resistant two parts epoxy repair putty paste compound: